Effect of cold working on oxidation behavior and nature of oxide film formed on carbon steel
Carbon steel is extensively used as a structural material in the secondary circuit of nuclear reactors. During fabrication of components such as elbows, T‐joint, expander/reducer, etc., the material is subjected to cold working. Aim of this study is to systematically investigate the effect of cold working on the oxidation behavior of carbon steel in alkaline environment at high temperature and pressure. Specimens from cold worked (up to 30%) carbon steel samples were oxidized in an autoclave at 270 °C for durations of up to 240 h in water of pH25 °C 10–10.2 obtained by adding lithium hydroxide. Oxidation rate, as calculated by weight gain, increased with extent of cold working. Potentiodynamic polarization and electrochemical impedance measurements were done in a borate buffer solution of pH 9.2 at room temperature, to characterize the oxide film formed on cold worked specimens. Impedance measurement followed by Mott–Schottky analysis showed that the defect density in the oxide increased with extent of cold working. Detailed examination established that the type and size of crystallites formed on the outermost oxide layer was the same irrespective of the extent of cold working.
Oxidation behavior and defect density in the oxide film of carbon steel was determined using weight measurement method and Mott–Schottky analysis respectively. Oxidation rate was increased with extent of cold working. Defect density in the oxide film determined by Mott−Schottky analysis was found to increase from 8.5 × 1021 to 2.2 × 1022 cm−3 with increase in extent of cold working up to 30%.
Congenital myasthenic syndromes (CMS) are heterogeneous disorders in which the safety margin of neuromuscular transmission is impaired by one or more specific mechanisms. Since the advent of next‐generation sequencing methods, the discovery of novel CMS targets and phenotypes ha ... mehr
Myasthenia gravis (MG) with antibodies to muscle‐specific kinase (MuSK) is characterized by fluctuating fatigable weakness. In MuSK MG, involvement of bulbar muscles, neck, and shoulder and respiratory weakness are more prominent than in acetylcholine receptor (AChR) MG. MuSK au ... mehr
Because of the failure of many promising therapeutics identified in preclinical evaluation, funding sources have established guidelines for increased rigor in animal evaluations. The myasthenia gravis (MG) community of scientists has developed guidelines for preclinical assessme ... mehr
John Wiley & Sons, Inc. stellt die Datenbank SpecInfo erstmals über die dynamische Internet-Plattform Wiley InterScience online zur Verfügung. Mit über 434 000 regelmäßig gepflegten Einträgen gehört SpecInfo zu den weltweit größten Spektrensammlungen.
SpecInfo bietet dem Benutzer eine int ... mehr